M-ZR multilayer HT+

M-ZR multilayer HT+

[Translate to Englisch:]

Super Translucent (5-layered pre-coloured)

Perfectly suitable for:

  • high aesthetic monolithic crowns and bridges (up to 3 units, including molar restorations)
  • especially for monolithic anterior restorations (bridgesup to 3 units)
  • cut back (one layer)
  • high aesthetic veneering
  • individual color gradients - which would otherwise only be possible with the extensive color-brush technique
  • High color reliability - due to the Multi Additive Technology®
  • Resistant to wrapping during sintering - due to individual isostatic redensification of each blank
     

Characteristics

Physical specifications

Physical Specifications Unit Value
Density (after sintering) [g/cm3] > 6,0
CTE (25 - 500°C) [10-6 K-1] ~ 10,0
Fracture toughness (SEVNB) [MPa√m] ~ 4,0
Fracture toughness (SEPB) [MPa√m] 2,4
Flexural strength [MPa] 750-800
E-Modulus [GPa] > 200

Chemical Composition

Chemical Composition [wt.%]
ZrO2 + HfO2 + Y2O3 ≥ 99,0
Al2O3 < 0,01
Other oxides ≤ 1,0
Y2O3 < 10,0

Technical Data

Technical Data
Type 5Y-TZP
Indication ISO 6872 type II, class 4 – Bridges with up to 3 limps incl. Molar restaurations
Colour percoloured acc. to VITA®
Aesthetics super translucent
Sintering temperatur 1.450 °C
CAM system open systems for Ø 98.5 mm blanks
Multi Additive Technology® reliable reproduction of colour via industrial colouring

Applications

  • Veneers
  • Inlays / Onlays
  • reduced Crown
  • full contour Crown anterior tooth
  • full contour Crown posterior tooth
  • Hybrid Abutment Crown
  • full contour Bridge (3-unit)
  • reduced Bridge (3-unit)

Range

Dimensions Ø 98.5 x 14 mm Ø 98.5 x 18 mm Ø 98.5 x 22 mm
Colour
A1
A2
A3
A3.5
B1
B2
C2
D3